Max size of aggregate and Nominal size of aggregate

Maximum size. The smallest sieve through which 100 percent of the aggregate sample particles pass.  Superpave defines the maximum aggregate size as "one sieve larger than the nominal maximum size"

Nominal maximum size. The largest sieve that retains some of the aggregate particles but generally not more than 10 percent by weight.  Superpave defines nominal maximum aggregate size as "one sieve size larger than the first sieve to retain more than 10 percent of the material"

Comments

Post a Comment

Popular posts from this blog

Why do we test concrete on 28th day? why not on 27th day or 29th day?

Before we go to the answer, we have to peep into the history of civil engineering. As we all know civil engineering and concrete technology were developed and practiced in England in ancient times and now US is leading in advancing the technology further. Concrete achieves its maximum material strength over its life time and depreciated by exposure and other environmental conditions. However, engineers with experience observed that about 99% of expected design strength was achieved in about 30 days and also observed that the rate of gaining strength was reducing thereafter making the concrete achieving its 100% design strength in a year or two. The Church was so powerful those days that it was compulsory for every citizen to attend Sunday prayer without fail. The defaulters were punished severely. If they had to test concrete on the 30th day, it may fall on a Sunday. In order to escape the punishment by the Church, the engineers had two choices - they have to test concrete cube o...
Read more

Cement IS 269

cement is used to bind the materials in concrete  The manufacturing process includes Proportioning of raw materials like chalk or limestone,Grinding and burning at 1400-1450OC in rotatory kiln. Due to intense heat the material becomes like spherical balls called clinkers. Gypsum is then added in 3-4%. Cement is formed by grinding the clinkers to required fineness. Tricalcium Silicate (C3S) hardens rapidly and is largely responsible for initial set and early strength. In general, the early strength of portland cement concrete is higher with increased percentages of C3S. Dicalcium Silicate (C2S) hardens slowly and contributes largely to strength increases at ages beyond 7 days. Tricalcium Aluminate (C3A) liberates a large amount of heat during the first few days of hardening and, together with C3S and C2S may somewhat increase the early strength of the hardening cement (this effect being due to the considerable heat of hydration that this compound evolves). It does affect set time...
Read more